Unsaturated Polyester Resins for
Marble Adhesives
| Marble Adhesive | Chemical Nature | Gel Time min | Performance | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 143 | Special | 5 - 8 | -Excellent adhesion to marble and stone. -Long gel time to give good workability time. --Fast surface drying during the curing. -Good storage stability. -Good curing at lower temperature. |
-Used as marble glue. |
| Egymoun UP 310 | Ortho | 5 - 8 | -Excellent adhesion to marble and stone. -Long gel time to give good workability time. -Fast surface drying during the curing. -Good storage stability. -Good curing at lower temperature. |
-Used as marble adhesive, Binder for highly filled knifing filler. |
Woad Coatings
| Wood | Chemical Nature | Gel Time min | Performance | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 210 | Special | 8 - 10 | -Air drying unsaturated polyester resin. -Long pot life. -Excellent adhesion to wood and metal. |
-Multi Purpose spray applications. |
| Egymoun UP 220 | Special | 8 - 10 | -Air drying unsaturated polyester resin. -Long pot life. -Excellent adhesion to wood and metal. |
-Multi Purpose resin, resist cracks, resist Styrene. |
| Egymoun UP 230 | Special | 8 - 10 | -Fast Tack-free, High gloss, Excellent Scratch and abrasion resistance. | -Wood topcoat and Sanding Sealer |
| Egymoun UP 240 | Special | 8 - 10 | -Fast Tack-free, Good Adhesions, Good Sandability and flexibility. | -Wood topcoat and Sanding Sealer |
| Egymoun UP 250 | Special | 8 - 10 | -Air Drying Unsaturated Polyester resin -very good sandability. -Fast surface drying during the curing. - Good storage stability. |
-Wood sanding sealer. |
Car refinish putties
<
| Car Refinish Putties | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 210 | Special | 8 - 10 | -Air drying unsaturated polyester resin. -Long pot life. -Excellent adhesion to wood and metal. |
-MIt can be used as a sole binder spray putty for car refinish. |
| Egymoun UP 220 | Special | 8 - 10 | Air drying unsaturated polyester resin. -High reactive, Midium viscosity. |
. It can be used as sole binder for the car refinish putty. |
| Egymoun UP 320 | Special | 7 - 9 | -Excellent sandability and adhesion to steel. -Long gel time to give good workability time. -Good wet ability of fillers. -Good storage stability. .-Good curing at lower temperature. |
-It can be used as sole binder for the car refinish putty. |
| Egymoun UP 350 | Special | 7 - 9 | -Excellent sandability and adhesion to steel. -Long gel time to give good workability time. -Good wet ability of fillers. -Good storage stability. .-Good curing at lower temperature. |
-It can be used as sole binder for the car refinish putty. |
| Egymoun UP 364 | Special | 7 - 9 | -Gives regid film after curing. -Excellent sandability and adhesion to steel. -Long gel time to give good workability time. -Good wet ability of fillers. -Good storage stability. .-Good curing at lower temperature. |
-It can be used with other resins like EGYMOUN UP-0371, UP-350 to increase their hardness in body filler. |
| Egymoun UP 371 | Special | 7 - 9 | -Gives regid film after curing. -Excellent sandability and adhesion to steel. -Long gel time to give good workability time. -Good wet ability of fillers. -Good storage stability. .-Good curing at lower temperature. |
-It can be used with other resins like EGYMOUN UP-0362, UP-350 to increase their Flexibility. |
| Egymoun UP 381 | Special | 7 - 9 | -Gives regid film after curing. -Excellent sandability and adhesion to steel. -Long gel time to give good workability time. -Good wet ability of fillers. -Good storage stability. .-Good curing at lower temperature. |
-It can be used in Unsaturated Polyester Putty for Galvanized Steel. |
Hand lay-up / spray-up
| Hand Lay Up/Spray Up | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 410 | Ortho | 15 - 25 | -Medium Viscosity. -Non preaccelerated, non thixotropic, Non waxed. |
-Multi Purpose Hand Lay Up applications. |
| Egymoun UP 413 | Ortho | 15 - 25 | -Resilient, Medium Viscosity. -Non preaccelerated, non thixotropic, Non waxed. |
-Water Tanks, Prefabricated cabins,Panels and Bath tubs |
| Egymoun UP 415 | Ortho | 15 - 27 | -Medium Reactive, Medium Viscosity. | -All types of Glassfibre reinforced moulding. |
| Egymoun UP 420 | Ortho | 15 - 27 | -Rigid , Medium Reactive, Medium Viscosity. | -It is recommended for all kinds of glassfibre reinforced moulding. |
| Egymoun UP 420 TL | Ortho | 15 - 27 | -Medium Reactive, Medium Viscosity , Thixotropic. | -Multi Purpose Hand Lay Up applications. |
Filament winding
| Filament Winding | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 406 | Ortho | 10 - 20 | -excellent mechanical properties, high resistance to heat deformation and high impact resistance. | -production of Pipes and centrifugal casting. |
| Egymoun UP 100 | ISO | 10 - 20 | -Medium reactive, medium viscosity, Good Chemical resistance. | -Manufacturing of Vessels, Pipes,ducts by filament winding and Gelcoats. |
| Egymoun UP 105 | Modified | 10 - 20 | -Flexible, Medium reactive, medium viscosity. | -Pipe fitting, filament winding application and food application. |
Infusion, Pultrusion and RTM
| Infusion, Pultrusion and RTM | Chemical Nature | Gel Time min | Performance | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 415 | Ortho | _____ | -Medium Reactive, L.V. | -General Purpose, Non Pre-Acclerated. |
| Egymoun UP 408 | Ortho | 7 - 10 | -excellent mechanical properties, high resistance to heat deformation and high impact resistance. | -Pultrusion Process and light pulls. |
| Egymoun UP 110 | ISO | 8 - 15 | -Pure resin, good witting and high elongation. | -Pultrusion Process, light pulls and electric structures. |
SMC and BMC
| SMC and BMC | Chemical Nature | Gel Time Sec | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 400 | Maleic | 80 - 140 | -High Reactive, Class A SMC. | -SMC and BMC for class A automotive application. |
| Egymoun UP 405 | Ortho | 80 - 140 | -High reactive. | -SMC and BMC with reduced tendency to crack. |
| Egymoun UP 115 | ISO | 80 - 140 | -High reactive, high heat destortion. | -SMC and BMC with reduced tendency to crack. |
Casting Resins
| Casting Resins | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 435 | Ortho | 5 - 10 | -High fillers loading, UV stabilized and good michanical properties. | -Cultured Marble, synthetic Marble. |
| Egymoun UP 440 | Ortho-NPG | 5 - 10 | -Good Chemical and heat resistance. | -Onyx. |
| Egymoun UP 120 | ISO-NPG | 5 - 10 | -Acrylic Modified, UV stabilized, Thermal shock stability and stain resisitance. | -Solid Surface. |
| Egymoun UP 490/td> | Ortho | 5 - 10 | -Plastizer, flexible resin. | -Flexibilizer, Wood Imitation. |
Chemical resistance
| Chemical Resistance | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 100 | ISO | 10 - 15 | -Medium reactive, medium viscosity, Good Hydrolysis resistance. | -Tanks, Vessels, Pipes, boats and Gelcoats. |
| Egymoun UP 110 | ISO | 15 - 20 | -Medium reactive, medium viscosity, Good Hydrolysis resistance. | -High quality Gelcoats, Tanks, pipes and boats. |
| Egymoun UP 120 | ISO-NPG | 10 - 15 | -High chemical resistance and Good electrical Properties. | -High resistance to Chemicals Tanks,Corrosion Protection, boats and Electrical Industry. |
Fire Retardant
| Fire Retardant | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 100 | HET | 10 - 20 | -Fire retardant resin. | _____ |
| Egymoun UP 110 | Special | 15 - 20 | -Medium reactive, medium viscosity, Good Hydrolysis resistance. | _____ |
Buttons
| Buttons | Chemical Nature | Gel Time min | Performance | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 460 | Ortho | 10 - 15 | -High reactive, Good Hydrolysis resistance, good color retension. | -buttons sheets and rods. |
| Egymoun UP 465 | Ortho | 15 - 20 | -Medium reactive,flixible, Good Hydrolysis resistance. | -buttons sheets and rods.td |
Acrylic Backup
| Acrylic Backup | Chemical Nature | Gel Time min | Performance | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 415 PT | Ortho | 10 - 15 | -Low reactive, preccelerated Thixotropic and high filler load. | -Backup for acrylic Bathtubs. |
| Egymoun UP 451 PT | Ortho | 15 - 20 | -Medium reactive,flixible, Good Hydrolysis resistance. | -Low reactive, medium viscosity, preccelerated and Thixotropic. |
Gelcoat
| Gelcoat | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 470 | Ortho | 15 - 25 | -exelent water resistance. | -Coating for boats and marine. |
| Egymoun UP 475 | Ortho | 15 - 25 | -White Pigmented, Accelerated excellent water resistance. | -Marine grade coating. |
| Egymoun UP 125 | ISO | 15 - 25 | -Accelerated and good chemical resistance. | -Marine coating for water tank, boats sanitary products. |
| Egymoun UP 130 | ISO-NPG | 15 - 20 | -White pigmentedm, Accelerated. | -Top coat for solid surface, kitchen tubs. |
Boats
| Boats | Chemical Nature | Gel Time min | Features | Suggested uses |
|---|---|---|---|---|
| Egymoun UP 421TP | Ortho | 20 - 30 | -Thixtropic, Preaccelerated. | -Boats, Yachts and Marine structures. |
| Egymoun UP 111 | ISO | 20 - 30 | -Thixtropic, Preaccelerated.and good chemical resistance. | -Boats, Yachts and Marine structures. |
Acrylic Polyol Resins for
Primers
| Primer | FOD% Solid Content | Solvents | Viscosity cP | Colour Max APHA | OH%(On Solid) | OH Value(mg KOH/g) |
|---|---|---|---|---|---|---|
| MOUNCRYL HA 518 | 53-56 | Xylene | 1000-2000 | 75 | 1.8 | 55-65 |
| MOUNCRYL HA 520 | 49-52 | Xylene | 600-1000 | 75 | 2 | 60-70 |
Basecoat paint
| Basecoat | FOD% Solid Content | Solvents | Viscosity cP | Colour Max APHA | OH%(On Solid) | OH Value(mg KOH/g) |
|---|---|---|---|---|---|---|
| MOUNCRYL TS 510 | 51-53 | Butyl Acetate | 1000-2000 | 100 | 2 | 60-70 |
| MOUNCRYL TS 515 | 65 | Butyl Acetate | 2000-3000 | 100 | _____ | _____ |
Clear coat
| Clear Coat | FOD% Solid Content | Solvents | Viscosity cP | Colour Max APHA | OH%(On Solid) | OH Value(mg KOH/g) |
|---|---|---|---|---|---|---|
| MOUNCRYL HA 525 | 64-66 | Butyl Acetate | 1200-2400 | 50 | 3 | 95-105 |
| MOUNCRYL HA 535 | 69-71 | Butyl Acetate | 3600-6000 | 100 | 4.5 | 90-120 |
Solid color top coat
| Solid Colors | FOD% Solid Content | Solvents | Viscosity cP | Colour Max APHA | OH%(On Solid) | OH Value(mg KOH/g) |
|---|---|---|---|---|---|---|
| MOUNCRYL HA 530 | 60-62 | Xylene / Butyl Acetate | 2800-4500 | 100 | 3 | 95-105 |
| MOUNCRYL HA 535 | 60-62 | Xylene / Butyl Acetate | 2800-4500 | 100 | 4.2 | 135-145 |
| MOUNCRYL HA 560 | 69-71 | Butyl Acetate | 3600-6000 | 100 | 4.5 | 90-120 |
Alkyd Resins for
Long Oil Alkyd Series
| Long Oil | Type | Solvent | N.V % | Colour G/ NV | Viscosity G at 25c | Acid Value | Features | Main Applications |
|---|---|---|---|---|---|---|---|---|
| S 65 T | Soya-bean Oil | White Spirit | 70, 58, 55 | Max. 7 at 50% | K to P | 5 - 10 | -Medium viscosity type with good brusability and excellent outdoor durability. | -Decorative enamels for interior and exterior use. -Undercoats and primers. |
| S 63 T | Soya-bean Oil | White Spirit | 70,58,55 | Max. 7 at 50% | K to P | 5 - 10 | -Medium viscosity type with good drying properties and excellent outdoor durability& lightand dark yellowing resistance. | -Marine paint, decorative paint, primer and undercoat. |
| S 63 T | Low rosin tall Oil fatty acid. | White Spirit | 70,60 | Max. 7 at 50% | T to Y | 5 - 10 | -High viscosity type with good brusability and very good drying properties. -Excellent outdoor durability and yellowing resistance. |
-Decorative enamels for interior and exterior use especially for white and light sheds |
| AR 63 T | Dehydrated castor Oil | White Spirit | 75,70 | Max. 7 at 50% | G to H | 5 - 10 | -Excellent adhesion, flexibility, yellowing resistance and outdoor durability. -Very good water resistance and drying properties. |
-Decorative enamels, varnishes for exterior use and to improve the flexibility of air drying alkyd resin. |
| L 68 T | Linseed Oil | White Spirit | 70 | Max. 7 at 50% | B to E | 5 - 10 | -Excellent brushability, gloss, surface draying and outdoor durability. | -Decorative enamels and undercoats. |
Medium Oil Alkyd Series
| Medium Oil | Type | Solvent | N.V % | Colour G/ NV | Viscosity G at 25c | Acid Value | Features | Main Applications |
|---|---|---|---|---|---|---|---|---|
| T 54 T | Low rosin tall Oil fatty acid | White Spirit | 55, 50 | Max. 7 at 50% | W to X | 5 - 10 | -High viscosity type with excellent gloss & gloss retention and outdoor durability. Very good yellowing resistance. | -Low cost primers &undercoats and high gloss decorative enamels. |
| S 48 T | Soya-bean Oil | White Spirit | 50 | Max. 7 at 50% | Z3 – Z 4 | 5 - 10 | -Extra high viscosity type with excellent gloss&gloss retention and outdoor durability. -good yellowing resistance. |
-Spray able enamels for semi industrial purposes. -Decorative enamels. |
| R 43 NT | Castor Oil | Xylene | 70, 50 | Max. 4 at 50% | W to X | 10 - 25 | -Excellent gloss &gloss retention and adhesion to metals surface when used in stoving enamels. -Good filling properties when used in cellulose nitrate lacquers. |
-Stoving enamels for steel surfaces. -Cellulose nitrate polishing for wood furniture’s. |
Short Oil Alkyd Series
| Short Oil | Type | Solvent | N.V % | Colour G/ NV | Viscosity G at 25c | Acid Value | Features | Main Applications |
|---|---|---|---|---|---|---|---|---|
| T 27 T | Low rosin tall Oil fatty acid | Xylene & Solvesso | 60,55,50 | Max. 3 at 50% | W to X | < 10 | -Extremely fast drying with good adhesion to steel surface. -Fast curing when combined with amino resin to produce stoving enaml. -Good yellowing resistance, even at elevated temperatures. -Compatible with cyclised and chlorinated rubber. |
-Stoving enamels, industrial finishes, fast drying and corrosion resistance primers. |
| S 27 T | Low rosin tall Oil fatty acid | Xylene & Solvesso | 60,55,50 | Max. 3 at 50% | W to X | < 10 | -Extremely fast drying with good adhesion to steel surface. -Fast curing when combined with amino resin to produce stoving enaml. -VeryGood yellowing resistance, even at elevated temperatures. -Compatible with cyclised and chlorinated rubber. |
-Stoving enamels , industrial finishes ,fast drying and corrosion resistance primers. |
| C 33 NT | Coconut Oil | Xylene | 60,55,50 | Max. 3 at 50% | R to S | < 10 | -Non drying resin but fast curing when combined with amino resin to produce stoving enamel. -Good yellowing resistance even at elevated temperatures. -Excellent combination of hardness, flexibility and outdoor durability. |
-Stoving enamels. Industrial finishes, clear and pigmented cellulose nitrate lacquers. |
Speciality & Other Resins
| Speciality & Other Resins Oil | Type | Solvent | N.V % | Colour G/ NV | Viscosity G at 25c | Acid Value | Features | Main Applications |
|---|---|---|---|---|---|---|---|---|
| ST 60 T | Styrene modified Soya bean and dehydrated castor Oil. | Xylene | 60 | Max. 7 at 50% | T to U | < 10 | -Very fast surface draying with excellent through-hardening when apply on metal surface. -Good gloss, hardness, waterand yellowing resistance. |
-Hammer finishes paints. -Quick drying sprayable paints for industrial purposes. |
| ML 100 | Non-plasticized melamine formaldehyde. | Isobutanol | 70 | 1 | Z4 to Z5 | 1 | _____ | _____ |